無鹵阻燃 WCV072-111 基礎(chǔ)創(chuàng)新塑料(美國)PPO 低密度 耐磨損 電線電纜

無鹵阻燃 WCV072-111 基礎(chǔ)創(chuàng)新塑料(美國)PPO 低密度 耐磨損 電線電纜 NORYL? WCV072 resinPolyphenylene Ether + PS + PPSABIC Innovative Plastics產(chǎn)品說明：Flexible, halogen free mPPE extrusion grade material for applications such as automotive wire insulation. Low specific gravity with good flame retardant and very good scrape abrasion resistance. Designed for evaluation in applications requiring ISO6722. 72 Shore D hardness. Processed using standard extrusion equipment.物性信息：基本信息添加劑阻燃性特性低密度良好耐磨損性無鹵阻燃性用途電線電纜應(yīng)用汽車領(lǐng)域的應(yīng)用物理性能額定值單位制測試方法比重1.03g/cm3ASTM D792, ISO 1183熔流率（熔體流動速率） (280°C/5.0 kg)14g/10 minASTM D1238溶化體積流率（MVR） (280°C/5.0 kg)13.4cm3/10minISO 1133吸水率ISO 62    飽和, 23°C0.12%ISO 62    平衡, 23°C, 50% RH0.050%ISO 62機(jī)械性能額定值單位制測試方法拉伸模量    -- 11710MPaASTM D638    --1760MPaISO 527-2/1抗張強(qiáng)度    屈服 243.8MPaASTM D638    屈服44.6MPaISO 527-2/50    斷裂 341.5MPaASTM D638    斷裂42.1MPaISO 527-2/50伸長率    屈服 415%ASTM D638    屈服11%ISO 527-2/50    斷裂 583%ASTM D638    斷裂46%ISO 527-2/50彎曲模量    50.0 mm 跨距 61560MPaASTM D790    -- 71750MPaISO 178彎曲應(yīng)力    --59.3MPaISO 178    屈服, 50.0 mm 跨距 853.2MPaASTM D790沖擊性能額定值單位制測試方法簡支梁缺口沖擊強(qiáng)度 9(23°C)34kJ/m2ISO 179/1eA懸壁梁缺口沖擊強(qiáng)度    -30°C67J/mASTM D256    23°C310J/mASTM D256    -30°C 106.9kJ/m2ISO 180/1A    23°C 1137kJ/m2ISO 180/1A裝有測量儀表的落鏢沖擊 (23°C, Total Energy)45.9JASTM D3763熱性能額定值單位制測試方法載荷下熱變形溫度    1.8 MPa, 未退火, 3.20 mm92.0°CASTM D648    1.8 MPa, 未退火, 64.0 mm 跨距 1298.0°CISO 75-2/Af維卡軟化溫度    --114°CASTM D1525, ISO 306/B50 10 13    --117°CISO 306/B120線形熱膨脹系數(shù)    流動 : -40 到 40°C8.5E-5cm/cm/°CASTM E831    流動 : -40 到 40°C8.4E-5cm/cm/°CISO 11359-2    橫向 : -40 到 40°C1.1E-4cm/cm/°CASTM E831, ISO 11359-2無鹵阻燃 WCV072-111 基礎(chǔ)創(chuàng)新塑料(美國)PPO 低密度 耐磨損 電線電纜 無鹵阻燃 WCV072-111 基礎(chǔ)創(chuàng)新塑料(美國)PPO 低密度 耐磨損 電線電纜